HMS3091A /100B

Products:

Easy

Dimensional stability

Alkali resistance, better heat resistance

Appropriate working hours

Better defoaming property

Uses:

1. Cultural Stone, GRC version of rocks, cement products copied.

2.UP, the large mold replication

3. Tin infusion products Copy

Specifications:

Hardness of 30-35 ° A

Operating time 30 ~ 40min

Touch time 1 ~ 2hr

Ejection time of 3 ~ 6hr

Tensile strength of 30 +2 kgf / cm ^

30-2 kgf / cm ^

Elongation of 400-100% 400 +100%

Tear strength of 14 +2 kgf / cm 14-2 kgf / cm

0.1% shrinkage

Operation:

1. Will be the main agent of about 1 to 2 minutes stirring, and then hardening agent into the mix 1 to 2 minutes, the speed of about 100 ~ 200rpm, do not high-speed stirring.

2. Into the vacuum devices vacuum of about 1 to 2 minutes, the exhaust about 2 times.

3. Out into the mold (the mold to be coated with release agent to facilitate demolding) natural flow levels, dry stripping.

4. Hardener recommended below 20 ℃ with 3.0%, 25 ℃ with 2.5%, 30 ℃ with 2.0% more than

* Can be adjusted according to demand dose hardening