| HTE
-401A / 401B
Uses:
• Industrial Supplies perfusion, then, impregnated, wear,
bearings, shoes mold
• embossed floor cement products such as copy
• MOLD perfusion
• Foam Application
Features:
• High Hardness 90-920A (1:1.5), 830A (1:1)
• easy
• dimensional stability
• High physical properties, high hardness
• better defoaming property
• High adhesion
• better resistance to alkali cement
Product Specifications ：
| HTE401A COLOR |
Dark yellowish translucent |
| Viscosity |
2,700 CPS |
catalyst
|
THE-401B |
| HTE401B COLOR |
transparent |
| Viscosity |
6,000 CPS |
| Mixing ratio wt：wt |
HTE401A：HTE401B (1：1.5) |
Operating time
|
10-15minutes |
Touch Time
|
30minutes |
Stripping Time
|
6hours |
| Hardness |
90 -92A |
| Tensile strength |
150 kgf/cm2 |
| Elongation |
250 |
| Tear strength |
52 kgf/cm |
| Shrinkage |
0.1% |
| Foam formulations |
In addition to these mixed ratio of plus 1% to 10% water,
to foam.
|
|
Product Operation:
1. First, the main agent of about 1 to 2 minutes stirring
standby (main agent will be micro-mat).
2, after weighing the hardener into the mixing drum first
lubricated bucket.
3, after weighing the main agent in the mixing drum into
the mix will be 1 to 2 minutes, turn
Speed of about 100 ~ 200rpm, do not high-speed stirring.
4. Into the vacuum devices vacuum of about 1 to 2 minutes,
the exhaust about 2 times.
5. Remove the natural flow into the mold level, dry stripping.
Note:
1. Sclerosing agent after use otherwise they will need to
cover the natural hardening of the lid can not be used.
2. Shorter operating time, use the required attention.
|