Introduction:
80°D。
Room temperature curing type, curing time is short.
Low viscosity, good maneuverability.
Transparent thin film coating.
Use:
Transparent for handicraft perfusion. Moisture-proof electrical
and electronic appliance parts, insulation, winding package
perfusion. Industrial Then, impregnation coating. Industrial
mold perfusion.
Specifications:
product base
color
|
Transparent |
| Viscosity |
14,000 CPS |
catalyst
|
THE 206LB |
| catalyst
color |
Transparent |
| Viscosity |
250 CPS |
| Mixing ratio wt：wt |
product base:catalyst
(2：1) |
operation time
|
30minutes(100g) |
Fully cured
|
about 2-4 hours
|
Tensile strength
|
282 kgf/cm2
|
Flexural strength
|
610 kgf/cm2
|
Shrinkage
|
less 0.1％
|
|
how to use:
1. The main agent and curing agent weight ratio of 2:1, stirring
about 2 to 3 minutes.
2. Into the vacuum devices vacuum 1 to 2 minutes, the exhaust
about 2 times (no vacuum equipment is free.)
3. Remove the brush, dipping, pour, roll can be.
Note: The ratio of the amount of more, shorter operation
time, easy to produce rapid hardening, the deployment should
be mixed according to the amount of operating conditions.
|