HTE5583A/B

Introduction:

● water-resistant, chemical resistance and excellent

● Operating time and hardening time is longer, thin and easy flow

● plane mobility, good flatness

● low viscosity, low heat

● moisture, insulation, good adhesion

● 8 ~ 16 hours at room temperature, 1 hour at 60 ℃

● Fully hardened

use:

For motors, electronics, electrical parts moisture, insulation perfusion

Specifications:

77 °D

operation time : 3-5hr /25。c 1hr/60。c

Full hardening : 10-20 hours/25 。c

Tensile : 215kgf / cm2

Flexural : 420kgf / cm2

Compressive : 620kgf / cm2

Shrinkage: 0.12%

Salt spray test :CNS 11581 K6855

Acid: 5%H2SO4

Alkaline : 5%NaOH

Withstanding Voltage: 14kv/mm

Shrinkage: 0.12%

dielectric constant (1MHz): 4.3MHz

product base：HTE5583A

color： Transparent

Viscosity： 2,000 CPS

capacity：300g

catalyst：HTE5583B

color：Transparent

Viscosity： 40 CPS

capacity：100g

Use ：

Stir in a cup first five minutes, and scrape the rubber cup attached, into the second cup, then continue stirring for three minutes, be sure to stir well, then pour into the mold. (Mixing time, mixing speed and the length of visible changes in the number of plastic materials can be hand-stirred with a stick, the machine set the stirring speed 500 rpm or less)