product base：HTE-5582A

color：dark brown

Viscosity(25℃)/CPS：3800 CPS

capacity：150g

catalyst：HTE-5582B

color： dark brown

Viscosity(25℃)/CPS：200 CPS

capacity：50g

Mixing Ratio A/B by Weight：

product base ：catalyst = 3： 1

application：Motors and electronic, electrical parts moisture, insulation perfusion

characteristics：Hardness 80 ° D hardness. Low viscosity, low heat. Water resistance, chemical resistance and excellent. Moisture, insulation, and then resistance.Shorter operating time and hardening time, the plane mobility, flat resistance.

Specifications

Use

operation time ：30-35 minutes/25℃

Hardening time：2-4 hours/25℃

Tensile (kgf/cm2)：243

Flexural (kgf/cm2)：410

Compressive (kgf/cm2)：670

Repeated hot and cold test：CNS 11581,K6855

Salt spray test ：CNS 11581,K6855

Moisture Resistance ：CNS 11581,K6855

Acid：5％Sulfuric acid

Alkaline：5％NaOH無龜裂

Volume resistance (Ω.cm) ： 2.3×1016

Withstanding Voltage (kv/mm) ： 15

Shrinkage(％) ： 0.2以下

dielectric constant (1MHz) ： 4.4

1. The main agent to be mixed before use.

2. And then the main agent and curing agent weight ratio of 3:1 that good mixing about 2 to 3 minutes.

3. Into the vacuum devices vacuum 1 to 2 minutes, the exhaust about 2 times, if no vacuum equipment is free.

4. Perfusion. (Ps. ratio of the amount of more, shorter operating time, easy to produce rapid hard

Technology, the deployment should be mixed according to the amount of operating conditions. )